Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelX2CrTi12 plate,X2CrTi12 Round Bar,X2CrTi12 forgings,X2CrTi12 suppliers, X2CrTi12 Stock,X2CrTi12 sheet, X2CrTi12 flat bar, X2CrTi12 pipe,X2CrTi12 tube,X2CrTi12 mould,X2CrTi12 round ingot,X2CrTi12 cold-rolled steel,X2CrTi12 coil,X2CrTi12 strap steel,X2CrTi12 hot-rolled steel,X2CrTi12 medium plate, X2CrTi12 heavy plate,X2CrTi12 shapped bar,X2CrTi12 hexahedral bar,X2CrTi12,X2CrTi12 slab ingot,X2CrTi12 slab,X2CrTi12 price,X2CrTi12 square bar,X2CrTi12 square steel,X2CrTi12 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of X2CrTi12.

Current Location:Home » Products » Alloy steel » X2CrTi12

Product category

X2CrTi12

Data Table for:Products: Alloy steel:X2CrTi12

X2CrTi12 properties and heat treatment forged piece, Including X2CrTi12 application and specifications, We have all specifications,Including X2CrTi12 steel plate, X2CrTi12 sheet, X2CrTi12 square steel, X2CrTi12 flat bar,X2CrTi12 round bar,X2CrTi12 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the X2CrTi12 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade X2CrTi12 and Standards

X2CrTi12 ( 1.4512 )

 

Grade :     X2CrTi12
    Number:     1.4512
    Standard: EN 10088 - 2 : 2005   stainless steels. Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
    Classification:     Ferritic stainless steels - Standard grade

Chemical composition % of the ladle analysis   of grade   X2CrTi12 (1.4512)

Ti= [6 * (C+N)] to 0.65
Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast.

C Si Mn P S Cr Ti
max   0.03 max   1 max   1 max   0.04 max   0.015 10.5 - 12.5 max   0.65

Equivalent grades of grade   X2CrTi12 (1.4512)

USA
-
France
AFNOR
England
BS
409
Z3CT12
409S




Machining performance

Download X2CrTi12 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.