Superalloys 1.4980, 1.4980, X6NiCrTiMoVB25.15.2, IncoloyA.286, Creep resisting steels, nickel and cobalt alloys to EN 10302: 2008

1.4980 Superalloys Properties Data

Chemical Composition of steel 1.4980 Superalloys: EN 10302: 2008 ,Cross Reference

1.4980 Superalloys Applications and Specifications

Note: a cold pull rods, round cakes and ring blank standard (Ti) 1.80% ~ 2.35%.
2 (B) of hot-rolled and cold-rolled sheet standard 0.003% ~ 0.010%, 2.00% or less (Mn), (P) acuities were 0.020%, 0.015% or less (S).
3 (Al) of cold drawn wire standard acuities were 0.35%, 1.75% ~ 2.35% (Ti) and (Si) 0.40% ~ 1.00%, 0.020% or less (P), (S) of 0.015% or less.
Use the wire, cold heading standards (Ti) 1.75% ~ 2.35%, 0.40% ~ 1.00% (Si), (P) acuities were 0.025%, 0.020% or less (S).
5 hot rolled and forged bar standard (Cu) of 0.25% or less.
1.5), heat treatment system is the standard heat treatment system are shown in table 1-3;Alloy is 900 ℃ heat treatment system plus or minus 10 ℃, 1 to 2 h, oil cooled to + 750 ℃ + 10 ℃, 16 h, air cooling.

  • EN 10302: 2008 - Creep resisting steels, nickel and cobalt alloys
  • EN 10269: 1999 - Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties
  • EN 10088-1: 2005 - Stainless steels. List of stainless steels

Mechanical properties at room temperature for 1.4980 Superalloys: EN 10302: 2008

Tensile Strength,Rm(MPa)

Yield Strength,Rp 0.2(MPa)

Impact,Kv/Ku(J)

Elongation,A(%)

Reduction of area,(%)

Hardness

Product shapes we supply:

Cross Reference, Equivalent, Similar of 1.4980 Superalloys grade:

1.4980 X6NiCrTiMoVB25-15-2 IncoloyA-286

Conditions & Properties

  • +A Soft annealed
  • +AC Annealed to achieve spheroidization of the carbides
  • +QT Quenched and tempered
  • +WW Warm worked
  • +N Normalized
  • +NT Normalized and tempered
  • +AT Solution annealed
  • +C Cold drawn / Hard
  • +CR Cold rolled
  • +PE Peeled
  • +T Tempered