Location » Home » Grades > Special Alloy > 6W6Mo5Cr4V

6W6Mo5Cr4V Enquiry | Print this page

Tags

Chemical composition % of the ladle analysis of grade 6W6Mo5Cr4V

C(％) Si(％) Mn(％) P(％) S(％) Cr(％) Ni(％) Mo(％) V(%) W(%) Cu(%)
0.55～0.65 ≤0.40 ≤0.60 ≤0.030 ≤0.030 3.70～4.30 ≤0.20 4.50～5.50 0.70～1.10 6.00～7.00 ≤0.30
  • » Alloy steel the performance characteristic and the USES(4)
  • » Alloy steel the performance characteristic and the USES(3)
  • » Alloy steel the performance characteristic and the USES(2)
  • » Alloy steel the performance characteristic and the USES(1)
    • Mechanical properties of grade 6W6Mo5Cr4V
    Proof strength
    Rp0.2 (MPa)    		 Tensile strength
    Rm (MPa)    		 Impact energy
    KV (J)    		 Elongation at fracture
    A (%)    		 Reduction in cross section on fracture
    Z (%)    		 As-Heat-Treated Condition Brinell hardness (HBW)
    615 (≥) 875 (≥) 44 22 32 Solution and Aging, Annealing, Ausaging, Q+T,etc 314
    Physical properties of grade 6W6Mo5Cr4V
    Property Density
    kg/dm3    		 Temperature T
    °C/F    		 Specific heat
    J / kgK    		 Thermal conductivity
    W/mK    		 Electric resistance
    µΩ·cm    		 Modulus of elasticity
    kN/mm2    		 Expansion rate
    298 (≥) 756 (≥) 21 13 43 Solution and Aging, Annealing, Ausaging, Q+T,etc 322
    Temp.
    °C/°F    		 Creep strain limit
    (10000h)
    (Rp1,0) N/mm2    		 Creep rupture strength
    (10000h)
    (Rp1,0) N/mm2
    667 656 611
    6W6Mo5Cr4V Range of products
    Product type Products Dimension Processes Deliver Status
    Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
    Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
    Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
    Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED