ГОСТ BЖЛl4 Enquiry | Print this page
- Category
- Type
- Steel grade
- Standard
- Country
- USE
- Grades
- Special Alloy
- » BЖЛl4
BЖЛ14H-BИ
BЖЛ18-BИ
BЖ4Л-BИ
BX9Л-BИ
ЖC3
ЖC3ЛK
ЖC6K
BЖЛ8
BЖЛ12y
BЖЛ12Э - ГОСТ
- Russia
- High temperature alloy castings
Chemical composition % of the ladle analysis of grade BЖЛl4
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | B(%) | Al(%) | Ti(%) |
| 0.05- 0.08 | 0.4 | 0.4 | Max 0.01 | 0.01 | 18.0- 20.0 | Balance | 4.5- 5.5 | 0.005 | 1.2- 1.5 | 2.6- 2.9 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 922 (≥) | 995 (≥) | 32 | 42 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 143 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 646 (≥) | 352 (≥) | 42 | 22 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 142 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 814 | 326 | 246 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |