EN EN NiCr23Co12Mo Enquiry | Print this page
- Category
- Type
- Steel grade
- Standard
- Country
- USE
- Grades
- Special Alloy
- » EN NiCr23Co12Mo
EN X5BCrMnNiN20-8
EN X85CrMoV18-2
EN CoCr20W15Ni
EN NiCo20Cr20MoTi
EN NiCr15Fe7Ti2Al
EN NiCr19Fe19Nb5Mo3
EN NiCr20Co13Mo4Ti3Al
EN NiCr20Co18Ti
EN NiCr20TiAl
EN NiCr22Fe18Mo - EN
- Euronorm
- Euronorm Stainless Steel
Chemical composition % of the ladle analysis of grade EN NiCr23Co12Mo
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Mo(％) | Ti(%) |
| 0.05-0.10 | 0.20 | 0.20 | 0.010 | 0.010 | 20.0-23.0 | 8.50-10.0 | 0.20-0.60 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 447 (≥) | 625 (≥) | 24 | 41 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 324 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 793 (≥) | 199 (≥) | 33 | 12 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 413 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 194 | 871 | 232 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |