EN EN X2CrNiMoN25-74 Enquiry | Print this page
- Category
- Type
- Steel grade
- Standard
- Country
- USE
- Grades
- Special Alloy
- » EN X2CrNiMoN25-74
EN X2CrNiMo17-123
EN X2Cr1NiMo18-14-3
EN X2CrNiMo18-10-4
EN X2CrNiMoCuN25-6-3
EN X2CrNiMoCuWN25-7-4
EN X2CrNiMoN17-11-2
EN X2CrNiMoN17-13-3
EN X2CrNiMoN17-13-5
EN X2CrNiMoN18-1Z-4
EN X2CrNiMnN22-5-3 - EN
- Euronorm
- Euronorm Stainless Steel
Chemical composition % of the ladle analysis of grade EN X2CrNiMoN25-74
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | N(%) |
| 0.030 | 1.00 | 2.00 | 0.035 | 0.015 | 24.0-26.0 | 6.00-8.00 | 3.00-4.50 | 0.20-0.35 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 399 (≥) | 192 (≥) | 43 | 13 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 323 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 263 (≥) | 654 (≥) | 13 | 31 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 242 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 897 | 447 | 437 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |