ISO ISO 19 Enquiry | Print this page
- Category
- Type
- Steel grade
- Standard
- Country
- USE
- Grades
- Special Alloy
- » ISO 19
ISO X10CrNiS18-9
ISO 17
ISO X3CrNiCu18-9-4
ISO X6CrNiTi18-10
ISO 15
ISO X7CrNiTi18-10
ISO X6CrNiNb18-10
ISO 16
ISO X7CrNiNb18-10
ISO X2CrNiMo17-12-2 - ISO
- ISO
- ISO standard thermal deformation of stainless steel
Chemical composition % of the ladle analysis of grade ISO 19
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | N(%) |
| Max 0.030 | Max 1.00 | Max 2.00 | Max 0.045 | Max 0.030 | 16.0-18.0 | 10.0-13.0 | 2.00-3.00 | Max 0.11 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 874 (≥) | 758 (≥) | 44 | 42 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 412 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 135 (≥) | 457 (≥) | 21 | 14 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 312 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 197 | 141 | 561 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| 00Cr19Ni10 | Carbon content lower than 0Cr19ni9 steel, excellent intergranular corrosion resistance, is used for welding after the class is not processed parts |
||
| 0Cr19Ni9N | Based on 0cr19ni9 plus N, strength increase and the plastic is not down. Reduce the thickness of the material. As a structure with strength components |
||
| 0Cr19Ni10NbN | Based on zero cr19ni9 plus N and Nb, with better than 0 cr19ni9 properties and USES |
||
| 0Cr19Ni13Mo3 | Seamless stainless steel tubes for boiler and heat exchanger |
||
| 00Cr19Ni13Mo3 | Seamless stainless steel tubes for boiler and heat exchanger |
||
| 1Cr19A13 | Heat-resisting steel sheets and plates |
||
| XM-19 | Chemical compositions of SAE wrought stainless steels |
||
| A 269 S21900 | Seamless and Welded Austenitic Stainless Steel Tubing for General Service |
||
| A 276 S21900 | Stainless Steel Bars and Shapes |
||
| A 314 S21900 | Seamless and Welded Austenitic Stainless Steel Tubing for General Service |
||
| A 473 S21900 | Stainless Steel Forgings |
||
| A 580 S21900 | Stainless Steel Wire |
||
| A 580 S21900 | Stainless Steel Wire |
||
| A 813 S21900 | Stainless Steel Wire |
||
| S21900 | Austenitic Chromium Manganese Nickel Stainless Steel |
||
| SA-813 S21900 | Specification for Single- or Double-Welded Austenitic Stainless Steel Pipe |
||
| SA-814 S21900 | Specification for Cold-Worked Welded Austenitic Stainless Steel Pipe |
||
| A 240 S21904 | Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications |
||
| A 269 S21904 | Seamless and Welded Austenitic Stainless Steel Tubing for General Service |
||
| A 276 S21904 | Stainless Steel Bars and Shapes |