ISO ISO H4 Enquiry | Print this page
- Category
- Type
- Steel grade
- Standard
- Country
- USE
- Grades
- Special Alloy
- » ISO H4
ISO X7CrNiAl17-7 wire
ISO X5CrNi18-10 strip
ISO X12CrNi17-7 strip
ISO X6CrNiMo17-12-2 strip
ISO X7CrNiAl17-7 strip
ISO X6CrTi12
ISO H1
ISO H2
ISO X10CrZlSi13
ISO H3 - ISO
- ISO
- ISO standard thermal deformation of stainless steel
Chemical composition % of the ladle analysis of grade ISO H4
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) |
| Max 0.080 | Max 1.00 | Max 1.00 | Max 0.040 | Max 0.030 | 16.0-18.0 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 591 (≥) | 677 (≥) | 44 | 12 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 244 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 954 (≥) | 418 (≥) | 24 | 32 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 324 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 589 | 522 | 399 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| GH4033 | Classification and designation for superalloys and high temperature intermetallic materials |
||
| GH4037 | Classification and designation for superalloys and high temperature intermetallic materials |
||
| GH4043 | Classification and designation for superalloys and high temperature intermetallic materials |
||
| GH4049 | Classification and designation for superalloys and high temperature intermetallic materials |
||
| GH4133 | Classification and designation for superalloys and high temperature intermetallic materials |
||
| GH4169 | Classification and designation for superalloys and high temperature intermetallic materials |
||
| GH4118 | Iron-based superalloy |
||
| GH4141 | Iron-based superalloy |
||
| GH4145 | Nickel-base superalloy |
||
| GH4146 | Nickel-base superalloy |
||
| GH4180 | Nickel-base superalloy |
||
| GH4220 | Nickel-base superalloy |
||
| GH4302 | Nickel-base superalloy |
||
| GH4698 | Nickel-base superalloy |
||
| GH4710 | Nickel-base superalloy |
||
| GH4738 | Nickel-base superalloy |
||
| GH4761 | Nickel-base superalloy |
||
| H41400 | Steel for intake valves |
||
| 09X16H4Б | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
||
| 20X13H4Γ9 | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |