L6
T1
T12001
T12002
T2
T4
T12004
T5
T12005
T6 - UNS
- USA
- Tungsten series High-Speed Tool Steel
Chemical composition % of the ladle analysis of grade T12006
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Mo(％) | V(%) | W(%) | Co(%) |
| 0.75～0.85 | 0.20～0.40 | 0.20～0.40 | ≤0.030 | ≤0.030 | 4.00～4.75 | 0.40～1.00 | 1.50～2.10 | 18.5～21.0 | 11.0～13.0 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 428 (≥) | 126 (≥) | 42 | 13 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 412 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 319 (≥) | 714 (≥) | 43 | 32 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 112 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 686 | 834 | 526 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| T12006 | High-Speed Tool Steel |