W9Mo3Cr4V
W6Mo5Cr4V2Al - China
- Saw high-speed tool steel hot-rolled steel strip
Chemical composition % of the ladle analysis of grade W9Mo3Cr4V coil
| C(％) | Si(％) | Cr(％) | Mo(％) | V(%) |
| 0.77～0.87 | 8.50～9.50 | 3.80～4.40 | 2.70～3.30 | 1.30～1.70 |
The decarburization layer depth (1) (2) / mm: Ⅰ) 0.02 Ⅱ) 0.04
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 499 (≥) | 727 (≥) | 44 | 12 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 311 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 547 (≥) | 559 (≥) | 43 | 13 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 114 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 158 | 597 | 433 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |