Stainless Steels - Special Steels X6CrNiTi18-10, X6CrNiTi18.10, 1.4541, X6CrNiTi18.10, 1.4541, X6CrNiTi18.10, X6CrNiTi18 10E, X6CrNiTi18.10, X6CrNiTi18.10, Stainless steels - Chemical composition to ISO 15510 (2010)

X6CrNiTi18-10 Stainless Steels - Special Steels Properties Data

Chemical Composition of steel X6CrNiTi18-10 Stainless Steels - Special Steels: ISO 15510 (2010) ,Cross Reference

X6CrNiTi18-10 Stainless Steels - Special Steels Applications and Specifications

Stainless steels - Chemical composition

  • ISO 15510 (2010) - Stainless steels -- Chemical composition
  • ISO 16143-1 (2004) - Stainless steels for general purposes -- Part 1: Flat products
  • ISO 16143-2 (2004) - Stainless steels for general purposes -- Part 2: Semi-finished products, bars, rods and sections
  • ISO 16143-3 (2005) - Stainless steels for general purposes -- Part 3: Wire
  • ISO 9327-5 - Steel forgings and rolled or forged bars for pressure purposes - Technical delivery conditions - Part 5: Stainless steels
  • ISO 9328-5 - Steel plates and strips for pressure purposes - Technical delivery conditions - Part 5: Weldable fine grain steels, thermomechanically rolled
  • ISO 9328-7 (2011) - Steel flat products for pressure purposes - Technical delivery conditions - Part 7: Stainless steels
  • ISO 9329-4 - Seamless steel tubes for pressure purposes - Technical delivery conditions - Part 4: Austenitic stainless steels
  • ISO 9330-6 - Welded steel tubes for pressure purposes - Technical delivery conditions - Part 6: Longitudinally welded austenitic stainless steel tubes
  • ISO/TS 15510 (2003) - Stainless steels - Chemical composition

Mechanical properties at room temperature for X6CrNiTi18-10 Stainless Steels - Special Steels: ISO 15510 (2010)

Tensile Strength,Rm(MPa)

Yield Strength,Rp 0.2(MPa)

Impact,Kv/Ku(J)

Elongation,A(%)

Reduction of area,(%)

Hardness

Product shapes we supply:

Cross Reference, Equivalent, Similar of X6CrNiTi18-10 Stainless Steels - Special Steels grade:

X6CrNiTi18-10 1.4541 X6CrNiTi18-10 1.4541 X6CrNiTi18-10 X6CrNiTi18 10E X6CrNiTi18-10 X6CrNiTi18-10

Conditions & Properties

  • +A Soft annealed
  • +AC Annealed to achieve spheroidization of the carbides
  • +QT Quenched and tempered
  • +WW Warm worked
  • +N Normalized
  • +NT Normalized and tempered
  • +AT Solution annealed
  • +C Cold drawn / Hard
  • +CR Cold rolled
  • +PE Peeled
  • +T Tempered