ГОСТ XH60Ю Enquiry | Print this page
- Category
- Type
- Steel grade
- Standard
- Country
- USE
- Grades
- Special Alloy
- » XH60Ю
XH38BT
XH45Ю
XH51BMTЮ/KΦK-BД
XH55MBЮ
XH55BMTΦK/Ю-BД
XH55BMTKЮ
XH56BMKЮ
XH56BMTЮ
XH57MTBЮ
XH58B - ГОСТ
- Russia
- Russia COST standard deformation of high temperature alloy
Chemical composition % of the ladle analysis of grade XH60Ю
| C(％) | Si(％) | Mn(％) | Cr(％) | Ni(％) | Al(%) | Other(%) |
| Max 0.10 | Max 0.80 | Max 0.30 | 15.0-18.0 | 55.0-58.0 | 2.60-3.50 | Ba: Max 0.10,Ce: Max 0.03 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 491 (≥) | 524 (≥) | 34 | 31 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 123 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 693 (≥) | 955 (≥) | 11 | 23 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 343 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 214 | 257 | 482 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| XH60Ю | Russia GOCT standard deformation of high temperature alloy grades and chemical composition |