- ISO standard Austenite size heat resistant steel
Chemical composition % of the ladle analysis of grade ISO H10
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) |
| Max 0.10 | Max 1.0 | Max 1.00 | Max 0.045 | Max 0.030 | 17.0-19.0 | 8.0-11.0 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 763 (≥) | 889 (≥) | 33 | 41 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 222 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 843 (≥) | 824 (≥) | 33 | 32 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 333 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 298 | 886 | 388 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| GH1015 | Solid solution strengthening type iron base alloy |
||
| GH1016 | Classification and designation for superalloys and high temperature intermetallic materials |
||
| GH1035 | Classification and designation for superalloys and high temperature intermetallic materials |
||
| GH1040 | Classification and designation for superalloys and high temperature intermetallic materials |
||
| GH1013 | Iron-based Superalloy |
||
| GH1014 | Iron-based superalloy |
||
| 04X18H10 | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
||
| 08X18H10 | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
||
| 08X18H10T | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
||
| 12X18H10T | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
||
| 12X18H10E | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
||
| 03X18H10 | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
||
| 03X19Ar3H10 | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
||
| 06X18H10T | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
||
| 09X18H10T | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
||
| 10X18H10T | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
||
| 25X18H10B2 | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
||
| ISO H10 | Stainless steels - Chemical composition |
||
| H10 | Hot-Work Tool Steel |
||
| H10 | Hot-Work Tool Steel |