1Cr18Ni11Ti
1Cr18Ni11Ti properties and heat treatment forged piece, Including 1Cr18Ni11Ti application and specifications, We have all specifications，Including 1Cr18Ni11Ti steel plate, 1Cr18Ni11Ti sheet, 1Cr18Ni11Ti square steel, 1Cr18Ni11Ti flat bar,1Cr18Ni11Ti round bar,1Cr18Ni11Ti forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the 1Cr18Ni11Ti has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade 1Cr18Ni11Ti and Standards
A basic introduction,
1 Cr18Ni11Ti Introduces basic Introduces basic
Second, chemical composition
1 Cr18Ni11Ti Chemical composition there environment
Carbon C: 0.04 ~ 0.10
Si Si: < 0.75
Manganese Mn: more than 2.0 0
P: more than 0.030 P
S: more than 0.030 sulfur
Chromium Cr: 17.00 ~ 20.00
Mo: avoid measurement molybdenum
Ni Ni: 9.00 ~ 13.00
Copper Cu: avoid measurement
Other: Ti4 * C ~ 0.60
Third, physical properties
1 Cr18Ni11Ti Physical properties of the Physical properties
1 Cr18Ni11Ti tensile test:
Steel thickness (mm) : from the point of measuring the yield point yield (MPa) sigma s: acuity 205 tensile strength tensile strength (MPa) sigma b: acuity 520
Four, material cross-references
1 Cr18Ni11Ti material that
Reference standard standard instead:
China GB13296-91 1 Cr18Ni11Ti
Material that will offer an Products: table
China GB13296-91 1 Cr18Ni11Ti
The United States ASTM A213M-94 bASTM A249M-94 a TP321H TP321H
Japan JIS G3463-94 SUS321HTB
British BS3605Part1-1991 321 S51
The French NF A49 217:1987-218:1979 NF A49 TUZ6CNT 1904-12-14 TUZ6CNT 18 ~ 10
ISO ISO 2604 out of the 75 TS 54
Five, the price
1 Cr18Ni11Ti supplier Suppliers-1 Cr18Ni11Ti
Six, production process
1 Cr18Ni11Ti Production process Production mode
Seven, characteristic USES
1 Cr18Ni11Ti characteristic Features use assumptions
Eight, heat treatment process
1 Cr18Ni11Ti Heat treatment process Heat treatment
Nine, Comments on Comments dr dr
1 Cr18Ni11Ti Comments on Comments dr dr
Machining performance
Download 1Cr18Ni11Ti the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.