Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel1.7357 plate,1.7357 Round Bar,1.7357 forgings,1.7357 suppliers, 1.7357 Stock,1.7357 sheet, 1.7357 flat bar, 1.7357 pipe,1.7357 tube,1.7357 mould,1.7357 round ingot,1.7357 cold-rolled steel,1.7357 coil,1.7357 strap steel,1.7357 hot-rolled steel,1.7357 medium plate, 1.7357 heavy plate,1.7357 shapped bar,1.7357 hexahedral bar,1.7357,1.7357 slab ingot,1.7357 slab,1.7357 price,1.7357 square bar,1.7357 square steel,1.7357 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 1.7357.

Current Location:Home » Products » Alloy steel » 1.7357

Product category

1.7357

Data Table for:Products: Alloy steel:1.7357

1.7357 properties and heat treatment forged piece, Including 1.7357 application and specifications, We have all specifications,Including 1.7357 steel plate, 1.7357 sheet, 1.7357 square steel, 1.7357 flat bar,1.7357 round bar,1.7357 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 1.7357 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 1.7357 and Standards

G17CrMo5-5 ( 1.7357 )

  Grade :     G17CrMo5-5
    Number:     1.7357
    Standard: EN 10213 : 2007   steel castings for pressure purposes
EN 10293 : 2005   steel castings for general engineering uses
    Classification:     Ferritic and martensitic

Chemical composition % of the ladle analysis   of grade   G17CrMo5-5 (1.7357)

For casting of ruling thickness < 28 mm, S =< 0.03 % (by mass) is permitted

C Si Mn Ni P S Cr Mo V Cu
0.15 - 0.2 max   0.6 0.5 - 1 max   0.4 max   0.02 max   0.02 1 - 1.5 0.45 - 0.65 max   0.05 max   0.3

Technological properties of grade   G17CrMo5-5 (1.7357) .

    Welding: ? Preheat temperature from 150 to 250 ? C; ? Interpass temperature max 350 ? C; ? Post Welding heat treatment >= 650 ? C;

Equivalent grades of grade   G17CrMo5-5 (1.7357)

China
GB
ZG20CrMoV




Machining performance

Download 1.7357 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.