Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel30CrNiMo8 plate,30CrNiMo8 Round Bar,30CrNiMo8 forgings,30CrNiMo8 suppliers, 30CrNiMo8 Stock,30CrNiMo8 sheet, 30CrNiMo8 flat bar, 30CrNiMo8 pipe,30CrNiMo8 tube,30CrNiMo8 mould,30CrNiMo8 round ingot,30CrNiMo8 cold-rolled steel,30CrNiMo8 coil,30CrNiMo8 strap steel,30CrNiMo8 hot-rolled steel,30CrNiMo8 medium plate, 30CrNiMo8 heavy plate,30CrNiMo8 shapped bar,30CrNiMo8 hexahedral bar,30CrNiMo8,30CrNiMo8 slab ingot,30CrNiMo8 slab,30CrNiMo8 price,30CrNiMo8 square bar,30CrNiMo8 square steel,30CrNiMo8 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 30CrNiMo8.

Current Location:Home » Products » Alloy steel » 30CrNiMo8

Product category

30CrNiMo8

Data Table for:Products: Alloy steel:30CrNiMo8

30CrNiMo8 properties and heat treatment forged piece, Including 30CrNiMo8 application and specifications, We have all specifications´╝îIncluding 30CrNiMo8 steel plate, 30CrNiMo8 sheet, 30CrNiMo8 square steel, 30CrNiMo8 flat bar,30CrNiMo8 round bar,30CrNiMo8 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 30CrNiMo8 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: ¤ć6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 30CrNiMo8 and Standards

30CrNiMo8 ( 1.6580 )

 

Grade :     30CrNiMo8
    Number:     1.6580
    Standard: EN 10083 - 3 : 2006   steels for quenching and tempering. Technical delivery conditions for alloy steels
    Classification:     steel without boron

 

Chemical composition % of the ladle analysis of grade 30CrNiMo8 (1.6580)

 

C Si Mn Ni P S Cr Mo
0.26 - 0.34 max   0.4 0.5 - 0.8 1.8 - 2.2 max   0.025 max   0.035 1.8 - 2.2 0.3 - 0.5

 

Equivalent grades of grade   30CrNiMo8 (1.6580)

 

Germany
DIN,WNr
France
AFNOR
England
BS
China
GB
Russia
GOST
International
ISO
30CrNiMo8
30CND8
823M30
30Cr2Ni2Mo
3KH3M3F
31CrNiMo8



Machining performance

Download 30CrNiMo8 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:30CrNiMo8 steel plate, 30CrNiMo8 sheet, 30CrNiMo8 square steel, 30CrNiMo8 flat bar,30CrNiMo8 round bar,30CrNiMo8 forgings