Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelA194 Gr 8M plate,A194 Gr 8M Round Bar,A194 Gr 8M forgings,A194 Gr 8M suppliers, A194 Gr 8M Stock,A194 Gr 8M sheet, A194 Gr 8M flat bar, A194 Gr 8M pipe,A194 Gr 8M tube,A194 Gr 8M mould,A194 Gr 8M round ingot,A194 Gr 8M cold-rolled steel,A194 Gr 8M coil,A194 Gr 8M strap steel,A194 Gr 8M hot-rolled steel,A194 Gr 8M medium plate, A194 Gr 8M heavy plate,A194 Gr 8M shapped bar,A194 Gr 8M hexahedral bar,A194 Gr 8M,A194 Gr 8M slab ingot,A194 Gr 8M slab,A194 Gr 8M price,A194 Gr 8M square bar,A194 Gr 8M square steel,A194 Gr 8M wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of A194 Gr 8M.

Current Location:Home » Products » Stainless Steel » A194 Gr 8M

Product category

A194 Gr 8M

Data Table for:Products: Stainless Steel:A194 Gr 8M

A194 Gr 8M properties and heat treatment forged piece, Including A194 Gr 8M application and specifications, We have all specifications´╝îIncluding A194 Gr 8M steel plate, A194 Gr 8M sheet, A194 Gr 8M square steel, A194 Gr 8M flat bar,A194 Gr 8M round bar,A194 Gr 8M forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the A194 Gr 8M has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: ¤ć6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade A194 Gr 8M and Standards

Price supply ASTM A194 / A320 Gr. 8, Gr. 8 m high pressure nut.
In the high and middle pressure valve; Sea, the ship, chemical, fluid engineering; Pressure vessels; Petrochemical equipment, and other high temperature and high pressure, low temperature high voltage equipment.
Optional exterior standard size: GB6170, GB6172, GB6175, DIN934, ANSI (UNC/UNF/UN) American standard coarse thread/fine teeth / 8 teeth permanent teeth, ANSI/ASME B18.2.2 American heavy, UNI5587 heavy, UNI5588, ASME B18.2.4.1 M, ASME B18.2.4.2 M, ASME B18.2.4.3 M, ASME B18.2.4.6 M metric hexagon nuts, etc.
Level in strict accordance with the ASTM A194 / A194M; ASME SA - 194 / SA - 194 m control.
Surface treatment: solution nature, coating teflon (PTFE), YFluo (fluorine polymer) coating, Xylan1424 coating, etc.




Machining performance

Download A194 Gr 8M the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:A194 Gr 8M steel plate, A194 Gr 8M sheet, A194 Gr 8M square steel, A194 Gr 8M flat bar,A194 Gr 8M round bar,A194 Gr 8M forgings