Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelAISI 216L plate,AISI 216L Round Bar,AISI 216L forgings,AISI 216L suppliers, AISI 216L Stock,AISI 216L sheet, AISI 216L flat bar, AISI 216L pipe,AISI 216L tube,AISI 216L mould,AISI 216L round ingot,AISI 216L cold-rolled steel,AISI 216L coil,AISI 216L strap steel,AISI 216L hot-rolled steel,AISI 216L medium plate, AISI 216L heavy plate,AISI 216L shapped bar,AISI 216L hexahedral bar,AISI 216L,AISI 216L slab ingot,AISI 216L slab,AISI 216L price,AISI 216L square bar,AISI 216L square steel,AISI 216L wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 216L.

Current Location:Home » Products » Stainless Steel » AISI 216L

Product category

AISI 216L

Data Table for:Products: Stainless Steel:AISI 216L

AISI 216L properties and heat treatment forged piece, Including AISI 216L application and specifications, We have all specifications,Including AISI 216L steel plate, AISI 216L sheet, AISI 216L square steel, AISI 216L flat bar,AISI 216L round bar,AISI 216L forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI 216L has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI 216L and Standards

C(%):    ≤0.03
Si(%):    ≤0.75
Mn(%):    7.50~9.00
P(%)≤:    0.045
S(%)≤:    0.03
Cr(%):    17.5~22.0
Ni(%):    5.00~7.00
Mo(%):    2.00~3.00
N 0.25~0.50




Machining performance

Download AISI 216L the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.