Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelAISI 303 plate,AISI 303 Round Bar,AISI 303 forgings,AISI 303 suppliers, AISI 303 Stock,AISI 303 sheet, AISI 303 flat bar, AISI 303 pipe,AISI 303 tube,AISI 303 mould,AISI 303 round ingot,AISI 303 cold-rolled steel,AISI 303 coil,AISI 303 strap steel,AISI 303 hot-rolled steel,AISI 303 medium plate, AISI 303 heavy plate,AISI 303 shapped bar,AISI 303 hexahedral bar,AISI 303,AISI 303 slab ingot,AISI 303 slab,AISI 303 price,AISI 303 square bar,AISI 303 square steel,AISI 303 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 303.

Current Location:Home » Products » Stainless Steel » AISI 303

Product category

AISI 303

Data Table for:Products: Stainless Steel:AISI 303

AISI 303 properties and heat treatment forged piece, Including AISI 303 application and specifications, We have all specifications,Including AISI 303 steel plate, AISI 303 sheet, AISI 303 square steel, AISI 303 flat bar,AISI 303 round bar,AISI 303 forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the AISI 303 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade AISI 303 and Standards

C(%):    ≤0.15
Si(%):    ≤1.00
Mn(%):    ≤2.00
P(%)≤:    0.2
S(%)≤:    ≥0.15
Cr(%):    17.0~19.0
Ni(%):    8.00~10.0
Mo(%):    —
Zr or Mo≤0.60

Machining performance

Download AISI 303 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.