Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelAISI 316LC plate,AISI 316LC Round Bar,AISI 316LC forgings,AISI 316LC suppliers, AISI 316LC Stock,AISI 316LC sheet, AISI 316LC flat bar, AISI 316LC pipe,AISI 316LC tube,AISI 316LC mould,AISI 316LC round ingot,AISI 316LC cold-rolled steel,AISI 316LC coil,AISI 316LC strap steel,AISI 316LC hot-rolled steel,AISI 316LC medium plate, AISI 316LC heavy plate,AISI 316LC shapped bar,AISI 316LC hexahedral bar,AISI 316LC,AISI 316LC slab ingot,AISI 316LC slab,AISI 316LC price,AISI 316LC square bar,AISI 316LC square steel,AISI 316LC wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 316LC.

Current Location:Home » Products » Stainless Steel » AISI 316LC

Product category


Data Table for:Products: Stainless Steel:AISI 316LC

AISI 316LC properties and heat treatment forged piece, Including AISI 316LC application and specifications, We have all specifications,Including AISI 316LC steel plate, AISI 316LC sheet, AISI 316LC square steel, AISI 316LC flat bar,AISI 316LC round bar,AISI 316LC forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the AISI 316LC has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade AISI 316LC and Standards

C(%): ≤0.03
Si(%): ≤1.00
Mn(%): ≤2.00
P(%)≤: 0.045
S(%)≤: 0.03
Cr(%): 16.0~18.0
Ni(%): 10.0~14.0
Mo(%): 1.75~2.75

Machining performance

Download AISI 316LC the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

Hot tags:AISI 316LC steel plate, AISI 316LC sheet, AISI 316LC square steel, AISI 316LC flat bar,AISI 316LC round bar,AISI 316LC forgings