Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelAISI 420F plate,AISI 420F Round Bar,AISI 420F forgings,AISI 420F suppliers, AISI 420F Stock,AISI 420F sheet, AISI 420F flat bar, AISI 420F pipe,AISI 420F tube,AISI 420F mould,AISI 420F round ingot,AISI 420F cold-rolled steel,AISI 420F coil,AISI 420F strap steel,AISI 420F hot-rolled steel,AISI 420F medium plate, AISI 420F heavy plate,AISI 420F shapped bar,AISI 420F hexahedral bar,AISI 420F,AISI 420F slab ingot,AISI 420F slab,AISI 420F price,AISI 420F square bar,AISI 420F square steel,AISI 420F wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 420F.

Current Location:Home » Products » Stainless Steel » AISI 420F

Product category


Data Table for:Products: Stainless Steel:AISI 420F

AISI 420F properties and heat treatment forged piece, Including AISI 420F application and specifications, We have all specifications,Including AISI 420F steel plate, AISI 420F sheet, AISI 420F square steel, AISI 420F flat bar,AISI 420F round bar,AISI 420F forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the AISI 420F has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade AISI 420F and Standards

 C(%): ≥0.15
Si(%): ≤1.00
Mn(%): ≤1.25
P(%)≤: 0.06
S(%)≤: ≥0.15
Cr(%): 12.0~14.0
Ni(%): —
Mo(%): ≤0.60

Machining performance

Download AISI 420F the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.