Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelASTM 309 plate,ASTM 309 Round Bar,ASTM 309 forgings,ASTM 309 suppliers, ASTM 309 Stock,ASTM 309 sheet, ASTM 309 flat bar, ASTM 309 pipe,ASTM 309 tube,ASTM 309 mould,ASTM 309 round ingot,ASTM 309 cold-rolled steel,ASTM 309 coil,ASTM 309 strap steel,ASTM 309 hot-rolled steel,ASTM 309 medium plate, ASTM 309 heavy plate,ASTM 309 shapped bar,ASTM 309 hexahedral bar,ASTM 309,ASTM 309 slab ingot,ASTM 309 slab,ASTM 309 price,ASTM 309 square bar,ASTM 309 square steel,ASTM 309 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM 309.

Current Location:Home » Products » Stainless Steel » ASTM 309

Product category

ASTM 309

Data Table for:Products: Stainless Steel:ASTM 309

ASTM 309 properties and heat treatment forged piece, Including ASTM 309 application and specifications, We have all specifications,Including ASTM 309 steel plate, ASTM 309 sheet, ASTM 309 square steel, ASTM 309 flat bar,ASTM 309 round bar,ASTM 309 forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the ASTM 309 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade ASTM 309 and Standards

C(%):    ≤0.20
Si(%):    ≤1.00
Mn(%):    ≤2.00
P(%)≤:    0.045
S(%)≤:    0.03
Cr(%):    22.0~24.0
Ni(%):    12.0~15.0

Machining performance

Download ASTM 309 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.