Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelASTM 309HCb plate,ASTM 309HCb Round Bar,ASTM 309HCb forgings,ASTM 309HCb suppliers, ASTM 309HCb Stock,ASTM 309HCb sheet, ASTM 309HCb flat bar, ASTM 309HCb pipe,ASTM 309HCb tube,ASTM 309HCb mould,ASTM 309HCb round ingot,ASTM 309HCb cold-rolled steel,ASTM 309HCb coil,ASTM 309HCb strap steel,ASTM 309HCb hot-rolled steel,ASTM 309HCb medium plate, ASTM 309HCb heavy plate,ASTM 309HCb shapped bar,ASTM 309HCb hexahedral bar,ASTM 309HCb,ASTM 309HCb slab ingot,ASTM 309HCb slab,ASTM 309HCb price,ASTM 309HCb square bar,ASTM 309HCb square steel,ASTM 309HCb wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM 309HCb.

Current Location:Home » Products » Stainless Steel » ASTM 309HCb

Product category


Data Table for:Products: Stainless Steel:ASTM 309HCb

ASTM 309HCb properties and heat treatment forged piece, Including ASTM 309HCb application and specifications, We have all specifications,Including ASTM 309HCb steel plate, ASTM 309HCb sheet, ASTM 309HCb square steel, ASTM 309HCb flat bar,ASTM 309HCb round bar,ASTM 309HCb forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the ASTM 309HCb has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade ASTM 309HCb and Standards

C(%): 0.04~0.10
Si(%): ≤0.75
Mn(%): ≤2.00
P(%)≤: 0.045
S(%)≤: 0.03
Cr(%): 22.0~24.0
Ni(%): 12.0~16.0
Mo(%): —

Machining performance

Download ASTM 309HCb the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.