Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelASTM 440C plate,ASTM 440C Round Bar,ASTM 440C forgings,ASTM 440C suppliers, ASTM 440C Stock,ASTM 440C sheet, ASTM 440C flat bar, ASTM 440C pipe,ASTM 440C tube,ASTM 440C mould,ASTM 440C round ingot,ASTM 440C cold-rolled steel,ASTM 440C coil,ASTM 440C strap steel,ASTM 440C hot-rolled steel,ASTM 440C medium plate, ASTM 440C heavy plate,ASTM 440C shapped bar,ASTM 440C hexahedral bar,ASTM 440C,ASTM 440C slab ingot,ASTM 440C slab,ASTM 440C price,ASTM 440C square bar,ASTM 440C square steel,ASTM 440C wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM 440C.

Current Location:Home » Products » Stainless Steel » ASTM 440C

Product category


Data Table for:Products: Stainless Steel:ASTM 440C

ASTM 440C properties and heat treatment forged piece, Including ASTM 440C application and specifications, We have all specifications,Including ASTM 440C steel plate, ASTM 440C sheet, ASTM 440C square steel, ASTM 440C flat bar,ASTM 440C round bar,ASTM 440C forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the ASTM 440C has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade ASTM 440C and Standards

 C(%): 0.95~1.20
Si(%): ≤1.00
Mn(%): ≤1.00
P(%)≤: 0.04
S(%)≤: 0.03
Cr(%): 16.0~18.0
Ni(%): —
Mo(%): ≤0.75

Machining performance

Download ASTM 440C the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

Hot tags:ASTM 440C steel plate, ASTM 440C sheet, ASTM 440C square steel, ASTM 440C flat bar,ASTM 440C round bar,ASTM 440C forgings