Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelASTM 446 plate,ASTM 446 Round Bar,ASTM 446 forgings,ASTM 446 suppliers, ASTM 446 Stock,ASTM 446 sheet, ASTM 446 flat bar, ASTM 446 pipe,ASTM 446 tube,ASTM 446 mould,ASTM 446 round ingot,ASTM 446 cold-rolled steel,ASTM 446 coil,ASTM 446 strap steel,ASTM 446 hot-rolled steel,ASTM 446 medium plate, ASTM 446 heavy plate,ASTM 446 shapped bar,ASTM 446 hexahedral bar,ASTM 446,ASTM 446 slab ingot,ASTM 446 slab,ASTM 446 price,ASTM 446 square bar,ASTM 446 square steel,ASTM 446 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM 446.

Current Location:Home » Products » Stainless Steel » ASTM 446

Product category

ASTM 446

Data Table for:Products: Stainless Steel:ASTM 446

ASTM 446 properties and heat treatment forged piece, Including ASTM 446 application and specifications, We have all specifications,Including ASTM 446 steel plate, ASTM 446 sheet, ASTM 446 square steel, ASTM 446 flat bar,ASTM 446 round bar,ASTM 446 forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the ASTM 446 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade ASTM 446 and Standards

C(%): ≤0.20
Si(%): 1
Mn(%): 1.5
P(%)≤: 0.04
S(%)≤: 0.03
Cr(%): 23.0~27.0
Ni(%): ≤0.50
Mo(%): —

Machining performance

Download ASTM 446 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

Hot tags:ASTM 446 steel plate, ASTM 446 sheet, ASTM 446 square steel, ASTM 446 flat bar,ASTM 446 round bar,ASTM 446 forgings