Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelASTM 502 plate,ASTM 502 Round Bar,ASTM 502 forgings,ASTM 502 suppliers, ASTM 502 Stock,ASTM 502 sheet, ASTM 502 flat bar, ASTM 502 pipe,ASTM 502 tube,ASTM 502 mould,ASTM 502 round ingot,ASTM 502 cold-rolled steel,ASTM 502 coil,ASTM 502 strap steel,ASTM 502 hot-rolled steel,ASTM 502 medium plate, ASTM 502 heavy plate,ASTM 502 shapped bar,ASTM 502 hexahedral bar,ASTM 502,ASTM 502 slab ingot,ASTM 502 slab,ASTM 502 price,ASTM 502 square bar,ASTM 502 square steel,ASTM 502 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM 502.

Current Location:Home » Products » Stainless Steel » ASTM 502

Product category

ASTM 502

Data Table for:Products: Stainless Steel:ASTM 502

ASTM 502 properties and heat treatment forged piece, Including ASTM 502 application and specifications, We have all specifications,Including ASTM 502 steel plate, ASTM 502 sheet, ASTM 502 square steel, ASTM 502 flat bar,ASTM 502 round bar,ASTM 502 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ASTM 502 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ASTM 502 and Standards

 C(%): ≤0.10
Si(%): ≤1.00
Mn(%): ≤1.00
P(%)≤: 0.04
S(%)≤: 0.03
Cr(%): 4.00~6.00
Ni(%): —
Mo(%): 0.40~0.65




Machining performance

Download ASTM 502 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:ASTM 502 steel plate, ASTM 502 sheet, ASTM 502 square steel, ASTM 502 flat bar,ASTM 502 round bar,ASTM 502 forgings