Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelASTM F46 plate,ASTM F46 Round Bar,ASTM F46 forgings,ASTM F46 suppliers, ASTM F46 Stock,ASTM F46 sheet, ASTM F46 flat bar, ASTM F46 pipe,ASTM F46 tube,ASTM F46 mould,ASTM F46 round ingot,ASTM F46 cold-rolled steel,ASTM F46 coil,ASTM F46 strap steel,ASTM F46 hot-rolled steel,ASTM F46 medium plate, ASTM F46 heavy plate,ASTM F46 shapped bar,ASTM F46 hexahedral bar,ASTM F46,ASTM F46 slab ingot,ASTM F46 slab,ASTM F46 price,ASTM F46 square bar,ASTM F46 square steel,ASTM F46 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM F46.

Current Location:Home » Products » Stainless Steel » ASTM F46

Product category


Data Table for:Products: Stainless Steel:ASTM F46

ASTM F46 properties and heat treatment forged piece, Including ASTM F46 application and specifications, We have all specifications,Including ASTM F46 steel plate, ASTM F46 sheet, ASTM F46 square steel, ASTM F46 flat bar,ASTM F46 round bar,ASTM F46 forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the ASTM F46 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade ASTM F46 and Standards

C(%): ≤0.018
Si(%): 3.70~4.30
Mn(%): ≤2.00
P(%)≤: 0.02
S(%)≤: 0.02
Cr(%): 17.0~18.5
Ni(%): 14.0~15.5
Mo(%): ≤0.20

Machining performance

Download ASTM F46 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.