Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelASTM F53 plate,ASTM F53 Round Bar,ASTM F53 forgings,ASTM F53 suppliers, ASTM F53 Stock,ASTM F53 sheet, ASTM F53 flat bar, ASTM F53 pipe,ASTM F53 tube,ASTM F53 mould,ASTM F53 round ingot,ASTM F53 cold-rolled steel,ASTM F53 coil,ASTM F53 strap steel,ASTM F53 hot-rolled steel,ASTM F53 medium plate, ASTM F53 heavy plate,ASTM F53 shapped bar,ASTM F53 hexahedral bar,ASTM F53,ASTM F53 slab ingot,ASTM F53 slab,ASTM F53 price,ASTM F53 square bar,ASTM F53 square steel,ASTM F53 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM F53.

Current Location:Home » Products » Stainless Steel » ASTM F53

Product category

ASTM F53

Data Table for:Products: Stainless Steel:ASTM F53

ASTM F53 properties and heat treatment forged piece, Including ASTM F53 application and specifications, We have all specifications,Including ASTM F53 steel plate, ASTM F53 sheet, ASTM F53 square steel, ASTM F53 flat bar,ASTM F53 round bar,ASTM F53 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ASTM F53 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ASTM F53 and Standards

 C(%): ≤0.030
Si(%): ≤0.80
Mn(%): ≤1.20
P(%)≤: 0.035
S(%)≤: 0.02
Cr(%): 24.0~26.0
Ni(%): 6.00~8.00
Mo(%): 3.00~5.00
Cu≤0.50,N 0.24~0.32




Machining performance

Download ASTM F53 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:ASTM F53 steel plate, ASTM F53 sheet, ASTM F53 square steel, ASTM F53 flat bar,ASTM F53 round bar,ASTM F53 forgings