Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelASTM WC9 plate,ASTM WC9 Round Bar,ASTM WC9 forgings,ASTM WC9 suppliers, ASTM WC9 Stock,ASTM WC9 sheet, ASTM WC9 flat bar, ASTM WC9 pipe,ASTM WC9 tube,ASTM WC9 mould,ASTM WC9 round ingot,ASTM WC9 cold-rolled steel,ASTM WC9 coil,ASTM WC9 strap steel,ASTM WC9 hot-rolled steel,ASTM WC9 medium plate, ASTM WC9 heavy plate,ASTM WC9 shapped bar,ASTM WC9 hexahedral bar,ASTM WC9,ASTM WC9 slab ingot,ASTM WC9 slab,ASTM WC9 price,ASTM WC9 square bar,ASTM WC9 square steel,ASTM WC9 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM WC9.

Current Location:Home » Products » Alloy steel » ASTM WC9

Product category

ASTM WC9

Data Table for:Products: Alloy steel:ASTM WC9

ASTM WC9 properties and heat treatment forged piece, Including ASTM WC9 application and specifications, We have all specifications,Including ASTM WC9 steel plate, ASTM WC9 sheet, ASTM WC9 square steel, ASTM WC9 flat bar,ASTM WC9 round bar,ASTM WC9 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ASTM WC9 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ASTM WC9 and Standards

C
Si
Mn
P
S
Cr Ni
0.05-0.18 0.6 0.4-0.7 0.04 0.045 2.0-2.75 0.5
Mo Al Cu Nb Ti W Ce
0.9-1.2   0.5     0.1  




Machining performance

Download ASTM WC9 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:ASTM WC9 steel plate, ASTM WC9 sheet, ASTM WC9 square steel, ASTM WC9 flat bar,ASTM WC9 round bar,ASTM WC9 forgings