Our to produce better steel-based products are the main used in industrial manufacturing various types High temperature high strength alloy and high-temperature alloyIncoloy 925 plate,Incoloy 925 Round Bar,Incoloy 925 forgings,Incoloy 925 suppliers, Incoloy 925 Stock,Incoloy 925 sheet, Incoloy 925 flat bar, Incoloy 925 pipe,Incoloy 925 tube,Incoloy 925 mould,Incoloy 925 round ingot,Incoloy 925 cold-rolled steel,Incoloy 925 coil,Incoloy 925 strap steel,Incoloy 925 hot-rolled steel,Incoloy 925 medium plate, Incoloy 925 heavy plate,Incoloy 925 shapped bar,Incoloy 925 hexahedral bar,Incoloy 925,Incoloy 925 slab ingot,Incoloy 925 slab,Incoloy 925 price,Incoloy 925 square bar,Incoloy 925 square steel,Incoloy 925 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Incoloy 925.

Current Location:Home » Products » High temperature high strength alloy and high-temperature alloy » Incoloy 925

Product category

Incoloy 925

Data Table for:Products: High temperature high strength alloy and high-temperature alloy:Incoloy 925

Incoloy 925 properties and heat treatment forged piece, Including Incoloy 925 application and specifications, We have all specifications,Including Incoloy 925 steel plate, Incoloy 925 sheet, Incoloy 925 square steel, Incoloy 925 flat bar,Incoloy 925 round bar,Incoloy 925 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Incoloy 925 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Incoloy 925 and Standards

General Characteristics of Incoloy™ 925
Incoloy™ 925 offers exceptional strength up to 1000°F (538°C). It’s a nickel-iron-chromium, age-hardenable alloy ideal for applications that require resistance to corrosion and pitting. Machinable and weldable, Incoloy™ 925 can be not and cold worked.

Chemical Composition of Incoloy™ 925
Nickel 42
Chromium 21
Molybdenum 3
Copper 2.2
Titanium 2.1
Aluminum 0.3
Carbon 0.02
Iron 32
Heat Treatment of Incoloy™ 925
Anneal by holding at 1800°F (982°C) for ½ to 1 hour, then rapidly cool (air cool small sections, water quench others)
Aging
Heat to 1400°F (760°C)
Hold at temperature 8 hours
Furnace cool at 100°F (38°C) per hour
Hold at 1150°F (621°C) for 8 hours
Air cool
Applications of Incoloy™ 925
Oil industry, including tool joints, tubular products, and parts for intermediate sour-gas wells
Fasteners
Pump and marine shafting
Strong, seamless piping and tubing
Machinability of Incoloy™ 925
Perform on hot-worked metal suggested to provide best finish while conserving machining
Workability of Incoloy™ 925
Hot working
Similar to Incoloy 825 up to 2000°F (1093°C) – higher temperatures produce a stronger, less-ductile metal
1600° to 2150°F (871°  to 1177°C) hot working range
Perform final hot working from 1600° to 1800°F (871° to 982°C) for top mechanical properties and best corrosion resistance
Cold working
Higher work-hardening rate than Incoloy 82




Machining performance

Download Incoloy 925 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Incoloy 925 steel plate, Incoloy 925 sheet, Incoloy 925 square steel, Incoloy 925 flat bar,Incoloy 925 round bar,Incoloy 925 forgings