Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelKaisaloy 45FG plate,Kaisaloy 45FG Round Bar,Kaisaloy 45FG forgings,Kaisaloy 45FG suppliers, Kaisaloy 45FG Stock,Kaisaloy 45FG sheet, Kaisaloy 45FG flat bar, Kaisaloy 45FG pipe,Kaisaloy 45FG tube,Kaisaloy 45FG mould,Kaisaloy 45FG round ingot,Kaisaloy 45FG cold-rolled steel,Kaisaloy 45FG coil,Kaisaloy 45FG strap steel,Kaisaloy 45FG hot-rolled steel,Kaisaloy 45FG medium plate, Kaisaloy 45FG heavy plate,Kaisaloy 45FG shapped bar,Kaisaloy 45FG hexahedral bar,Kaisaloy 45FG,Kaisaloy 45FG slab ingot,Kaisaloy 45FG slab,Kaisaloy 45FG price,Kaisaloy 45FG square bar,Kaisaloy 45FG square steel,Kaisaloy 45FG wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Kaisaloy 45FG.

Current Location:Home » Products » Carbon steel » Kaisaloy 45FG

Product category

Kaisaloy 45FG

Data Table for:Products: Carbon steel:Kaisaloy 45FG

Kaisaloy 45FG properties and heat treatment forged piece, Including Kaisaloy 45FG application and specifications, We have all specifications,Including Kaisaloy 45FG steel plate, Kaisaloy 45FG sheet, Kaisaloy 45FG square steel, Kaisaloy 45FG flat bar,Kaisaloy 45FG round bar,Kaisaloy 45FG forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Kaisaloy 45FG has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Kaisaloy 45FG and Standards

C(%):    0.12
Si(%):    0.50
Mn(%):    0.60
Cr(%):    0.25
Ni(%):    0.60
Cu(%):    ≥0.30
Nb(%):    —
V(%):    ≥0.02




Machining performance

Download Kaisaloy 45FG the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Kaisaloy 45FG steel plate, Kaisaloy 45FG sheet, Kaisaloy 45FG square steel, Kaisaloy 45FG flat bar,Kaisaloy 45FG round bar,Kaisaloy 45FG forgings