Our to produce better steel-based products are the main used in industrial manufacturing various types Nickel base alloy and high nickel containing steelsNiMo16Cr15W plate,NiMo16Cr15W Round Bar,NiMo16Cr15W forgings,NiMo16Cr15W suppliers, NiMo16Cr15W Stock,NiMo16Cr15W sheet, NiMo16Cr15W flat bar, NiMo16Cr15W pipe,NiMo16Cr15W tube,NiMo16Cr15W mould,NiMo16Cr15W round ingot,NiMo16Cr15W cold-rolled steel,NiMo16Cr15W coil,NiMo16Cr15W strap steel,NiMo16Cr15W hot-rolled steel,NiMo16Cr15W medium plate, NiMo16Cr15W heavy plate,NiMo16Cr15W shapped bar,NiMo16Cr15W hexahedral bar,NiMo16Cr15W,NiMo16Cr15W slab ingot,NiMo16Cr15W slab,NiMo16Cr15W price,NiMo16Cr15W square bar,NiMo16Cr15W square steel,NiMo16Cr15W wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of NiMo16Cr15W.

Current Location:Home » Products » Nickel base alloy and high nickel containing steels » NiMo16Cr15W

Product category

NiMo16Cr15W

Data Table for:Products: Nickel base alloy and high nickel containing steels:NiMo16Cr15W

NiMo16Cr15W properties and heat treatment forged piece, Including NiMo16Cr15W application and specifications, We have all specifications,Including NiMo16Cr15W steel plate, NiMo16Cr15W sheet, NiMo16Cr15W square steel, NiMo16Cr15W flat bar,NiMo16Cr15W round bar,NiMo16Cr15W forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the NiMo16Cr15W has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade NiMo16Cr15W and Standards

Material number 2.4819 - NiMo16Cr15W

Composition in % :

C
Si
Mn
P
S
Cr
Mo
Ni
max. 0,01
max. 0,08
max. 1,00
max. 0,025
max. 0,015
14,50 - 16,50
15,00 - 17,00
51,00 - 63,00

 
 

V
W
Ti
Cu
Al
Nb
Co
Fe
max. 0,35
3,00 - 4,50
 
max. 0,50
 
 
max. 2,50
4,00 - 7,00

 

Range of application and heat treatment :

Nickel alloy : chemistry industry , paper industry
Solution annealing : 1100 - 1160 °C (water)
 

General and distinctive features :




Machining performance

Download NiMo16Cr15W the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.