Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelOrelloy 242 plate,Orelloy 242 Round Bar,Orelloy 242 forgings,Orelloy 242 suppliers, Orelloy 242 Stock,Orelloy 242 sheet, Orelloy 242 flat bar, Orelloy 242 pipe,Orelloy 242 tube,Orelloy 242 mould,Orelloy 242 round ingot,Orelloy 242 cold-rolled steel,Orelloy 242 coil,Orelloy 242 strap steel,Orelloy 242 hot-rolled steel,Orelloy 242 medium plate, Orelloy 242 heavy plate,Orelloy 242 shapped bar,Orelloy 242 hexahedral bar,Orelloy 242,Orelloy 242 slab ingot,Orelloy 242 slab,Orelloy 242 price,Orelloy 242 square bar,Orelloy 242 square steel,Orelloy 242 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Orelloy 242.

Current Location:Home » Products » Carbon steel » Orelloy 242

Product category

Orelloy 242

Data Table for:Products: Carbon steel:Orelloy 242

Orelloy 242 properties and heat treatment forged piece, Including Orelloy 242 application and specifications, We have all specifications,Including Orelloy 242 steel plate, Orelloy 242 sheet, Orelloy 242 square steel, Orelloy 242 flat bar,Orelloy 242 round bar,Orelloy 242 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Orelloy 242 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Orelloy 242 and Standards

C(%):    0.25
Si(%):    0.30
Mn(%):    1.35
Cr(%):    0.40~0.65
Ni(%):    -
Cu(%):    ≥0.20




Machining performance

Download Orelloy 242 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Orelloy 242 steel plate, Orelloy 242 sheet, Orelloy 242 square steel, Orelloy 242 flat bar,Orelloy 242 round bar,Orelloy 242 forgings