Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelSAE G6 plate,SAE G6 Round Bar,SAE G6 forgings,SAE G6 suppliers, SAE G6 Stock,SAE G6 sheet, SAE G6 flat bar, SAE G6 pipe,SAE G6 tube,SAE G6 mould,SAE G6 round ingot,SAE G6 cold-rolled steel,SAE G6 coil,SAE G6 strap steel,SAE G6 hot-rolled steel,SAE G6 medium plate, SAE G6 heavy plate,SAE G6 shapped bar,SAE G6 hexahedral bar,SAE G6,SAE G6 slab ingot,SAE G6 slab,SAE G6 price,SAE G6 square bar,SAE G6 square steel,SAE G6 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of SAE G6.

Current Location:Home » Products » Tool steel » SAE G6

Product category

SAE G6

Data Table for:Products: Tool steel:SAE G6

SAE G6 properties and heat treatment forged piece, Including SAE G6 application and specifications, We have all specifications,Including SAE G6 steel plate, SAE G6 sheet, SAE G6 square steel, SAE G6 flat bar,SAE G6 round bar,SAE G6 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the SAE G6 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade SAE G6 and Standards

C
Si
Mn
P
S
Cr Ni
0.55 0.25 0.8     1.0  
Mo Al Cu Nb Ti V Ce
0.45         0.1  




Machining performance

Download SAE G6 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.