Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelSAE P4 plate,SAE P4 Round Bar,SAE P4 forgings,SAE P4 suppliers, SAE P4 Stock,SAE P4 sheet, SAE P4 flat bar, SAE P4 pipe,SAE P4 tube,SAE P4 mould,SAE P4 round ingot,SAE P4 cold-rolled steel,SAE P4 coil,SAE P4 strap steel,SAE P4 hot-rolled steel,SAE P4 medium plate, SAE P4 heavy plate,SAE P4 shapped bar,SAE P4 hexahedral bar,SAE P4,SAE P4 slab ingot,SAE P4 slab,SAE P4 price,SAE P4 square bar,SAE P4 square steel,SAE P4 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of SAE P4.

Current Location:Home » Products » Tool steel » SAE P4

Product category

SAE P4

Data Table for:Products: Tool steel:SAE P4

SAE P4 properties and heat treatment forged piece, Including SAE P4 application and specifications, We have all specifications,Including SAE P4 steel plate, SAE P4 sheet, SAE P4 square steel, SAE P4 flat bar,SAE P4 round bar,SAE P4 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the SAE P4 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade SAE P4 and Standards

C
Si
Mn
P
S
Cr Ni
0.12 0.1-0.4 0.2-0.6 0.03 0.03 4.0-5.25 ≤0.35
Mo Al Cu Nb Ti V Ce
0.4-1.0            




Machining performance

Download SAE P4 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:SAE P4 steel plate, SAE P4 sheet, SAE P4 square steel, SAE P4 flat bar,SAE P4 round bar,SAE P4 forgings