Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelStelcoloy 50 plate,Stelcoloy 50 Round Bar,Stelcoloy 50 forgings,Stelcoloy 50 suppliers, Stelcoloy 50 Stock,Stelcoloy 50 sheet, Stelcoloy 50 flat bar, Stelcoloy 50 pipe,Stelcoloy 50 tube,Stelcoloy 50 mould,Stelcoloy 50 round ingot,Stelcoloy 50 cold-rolled steel,Stelcoloy 50 coil,Stelcoloy 50 strap steel,Stelcoloy 50 hot-rolled steel,Stelcoloy 50 medium plate, Stelcoloy 50 heavy plate,Stelcoloy 50 shapped bar,Stelcoloy 50 hexahedral bar,Stelcoloy 50,Stelcoloy 50 slab ingot,Stelcoloy 50 slab,Stelcoloy 50 price,Stelcoloy 50 square bar,Stelcoloy 50 square steel,Stelcoloy 50 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Stelcoloy 50.

Current Location:Home » Products » Carbon steel » Stelcoloy 50

Product category

Stelcoloy 50

Data Table for:Products: Carbon steel:Stelcoloy 50

Stelcoloy 50 properties and heat treatment forged piece, Including Stelcoloy 50 application and specifications, We have all specifications,Including Stelcoloy 50 steel plate, Stelcoloy 50 sheet, Stelcoloy 50 square steel, Stelcoloy 50 flat bar,Stelcoloy 50 round bar,Stelcoloy 50 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Stelcoloy 50 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Stelcoloy 50 and Standards

C(%):    0.15
Si(%):    0.15~0.30
Mn(%):    1.35
Cr(%):    0.30~0.50
Ni(%):    0.25~0.50
Cu(%):    0.20~0.50
Nb(%):    -
V(%):    ≥0.01




Machining performance

Download Stelcoloy 50 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Stelcoloy 50 steel plate, Stelcoloy 50 sheet, Stelcoloy 50 square steel, Stelcoloy 50 flat bar,Stelcoloy 50 round bar,Stelcoloy 50 forgings