Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi-6Al-2Nb-1Ta-1Mo plate,Ti-6Al-2Nb-1Ta-1Mo Round Bar,Ti-6Al-2Nb-1Ta-1Mo forgings,Ti-6Al-2Nb-1Ta-1Mo suppliers, Ti-6Al-2Nb-1Ta-1Mo Stock,Ti-6Al-2Nb-1Ta-1Mo sheet, Ti-6Al-2Nb-1Ta-1Mo flat bar, Ti-6Al-2Nb-1Ta-1Mo pipe,Ti-6Al-2Nb-1Ta-1Mo tube,Ti-6Al-2Nb-1Ta-1Mo mould,Ti-6Al-2Nb-1Ta-1Mo round ingot,Ti-6Al-2Nb-1Ta-1Mo cold-rolled steel,Ti-6Al-2Nb-1Ta-1Mo coil,Ti-6Al-2Nb-1Ta-1Mo strap steel,Ti-6Al-2Nb-1Ta-1Mo hot-rolled steel,Ti-6Al-2Nb-1Ta-1Mo medium plate, Ti-6Al-2Nb-1Ta-1Mo heavy plate,Ti-6Al-2Nb-1Ta-1Mo shapped bar,Ti-6Al-2Nb-1Ta-1Mo hexahedral bar,Ti-6Al-2Nb-1Ta-1Mo,Ti-6Al-2Nb-1Ta-1Mo slab ingot,Ti-6Al-2Nb-1Ta-1Mo slab,Ti-6Al-2Nb-1Ta-1Mo price,Ti-6Al-2Nb-1Ta-1Mo square bar,Ti-6Al-2Nb-1Ta-1Mo square steel,Ti-6Al-2Nb-1Ta-1Mo wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti-6Al-2Nb-1Ta-1Mo.

Current Location:Home » Products » Ti Alloy » Ti-6Al-2Nb-1Ta-1Mo

Product category

Ti-6Al-2Nb-1Ta-1Mo

Data Table for:Products: Ti Alloy:Ti-6Al-2Nb-1Ta-1Mo

Ti-6Al-2Nb-1Ta-1Mo properties and heat treatment forged piece, Including Ti-6Al-2Nb-1Ta-1Mo application and specifications, We have all specifications´╝îIncluding Ti-6Al-2Nb-1Ta-1Mo steel plate, Ti-6Al-2Nb-1Ta-1Mo sheet, Ti-6Al-2Nb-1Ta-1Mo square steel, Ti-6Al-2Nb-1Ta-1Mo flat bar,Ti-6Al-2Nb-1Ta-1Mo round bar,Ti-6Al-2Nb-1Ta-1Mo forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti-6Al-2Nb-1Ta-1Mo has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: ¤ć6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti-6Al-2Nb-1Ta-1Mo and Standards

Category  Titanium Alloy
Class  Wrought
Type  Near alpha alloy
Designations  United States: MIL-T-9046

Composition
Element Weight %
Al  6 
Nb  2 
Ta  1 
Mo  1 

Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 4.48 25  
Poisson's Ratio 0.33 25  
Elastic Modulus (GPa) 113.8 25  
Tensile Strength (Mpa) 855  25  rolled (mm plate (25 mm)) 
Yield Strength (Mpa) 758 
Elongation (%) 13 
Reduction in Area (%) 34 
Hardness (HRC) 30  25  rolled (plate (25 mm)) 
Impact Strength (J)
(Charpy)
31  25  rolled (plate (25 mm)) 

Thermal Properties
Properties  Conditions 
T (°C) Treatment
Thermal Expansion (10-6/ºC) 9  20-650  




Machining performance

Download Ti-6Al-2Nb-1Ta-1Mo the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.