Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelUNS S17600 plate,UNS S17600 Round Bar,UNS S17600 forgings,UNS S17600 suppliers, UNS S17600 Stock,UNS S17600 sheet, UNS S17600 flat bar, UNS S17600 pipe,UNS S17600 tube,UNS S17600 mould,UNS S17600 round ingot,UNS S17600 cold-rolled steel,UNS S17600 coil,UNS S17600 strap steel,UNS S17600 hot-rolled steel,UNS S17600 medium plate, UNS S17600 heavy plate,UNS S17600 shapped bar,UNS S17600 hexahedral bar,UNS S17600,UNS S17600 slab ingot,UNS S17600 slab,UNS S17600 price,UNS S17600 square bar,UNS S17600 square steel,UNS S17600 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS S17600.

Current Location:Home » Products » Stainless Steel » UNS S17600

Product category

UNS S17600

Data Table for:Products: Stainless Steel:UNS S17600

UNS S17600 properties and heat treatment forged piece, Including UNS S17600 application and specifications, We have all specifications,Including UNS S17600 steel plate, UNS S17600 sheet, UNS S17600 square steel, UNS S17600 flat bar,UNS S17600 round bar,UNS S17600 forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the UNS S17600 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade UNS S17600 and Standards

C(%):    ≤0.08
Si(%):    ≤1.00
Mn(%):    ≤1.00
P(%)≤:    0.04
S(%)≤:    0.03
Cr(%):    16.0~17.5

Machining performance

Download UNS S17600 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.