Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelUNS S31603 plate,UNS S31603 Round Bar,UNS S31603 forgings,UNS S31603 suppliers, UNS S31603 Stock,UNS S31603 sheet, UNS S31603 flat bar, UNS S31603 pipe,UNS S31603 tube,UNS S31603 mould,UNS S31603 round ingot,UNS S31603 cold-rolled steel,UNS S31603 coil,UNS S31603 strap steel,UNS S31603 hot-rolled steel,UNS S31603 medium plate, UNS S31603 heavy plate,UNS S31603 shapped bar,UNS S31603 hexahedral bar,UNS S31603,UNS S31603 slab ingot,UNS S31603 slab,UNS S31603 price,UNS S31603 square bar,UNS S31603 square steel,UNS S31603 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS S31603.

Current Location:Home » Products » Stainless Steel » UNS S31603

Product category

UNS S31603

Data Table for:Products: Stainless Steel:UNS S31603

UNS S31603 properties and heat treatment forged piece, Including UNS S31603 application and specifications, We have all specifications,Including UNS S31603 steel plate, UNS S31603 sheet, UNS S31603 square steel, UNS S31603 flat bar,UNS S31603 round bar,UNS S31603 forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the UNS S31603 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade UNS S31603 and Standards

C(%): ≤0.03
Si(%): ≤1.00
Mn(%): ≤2.00
P(%)≤: 0.045
S(%)≤: 0.03
Cr(%): 16.0~18.0
Ni(%): 10.0~14.0
Mo(%): 2.00~3.00

Machining performance

Download UNS S31603 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.