Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelUNS S44004 plate,UNS S44004 Round Bar,UNS S44004 forgings,UNS S44004 suppliers, UNS S44004 Stock,UNS S44004 sheet, UNS S44004 flat bar, UNS S44004 pipe,UNS S44004 tube,UNS S44004 mould,UNS S44004 round ingot,UNS S44004 cold-rolled steel,UNS S44004 coil,UNS S44004 strap steel,UNS S44004 hot-rolled steel,UNS S44004 medium plate, UNS S44004 heavy plate,UNS S44004 shapped bar,UNS S44004 hexahedral bar,UNS S44004,UNS S44004 slab ingot,UNS S44004 slab,UNS S44004 price,UNS S44004 square bar,UNS S44004 square steel,UNS S44004 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS S44004.

Current Location:Home » Products » Stainless Steel » UNS S44004

Product category

UNS S44004

Data Table for:Products: Stainless Steel:UNS S44004

UNS S44004 properties and heat treatment forged piece, Including UNS S44004 application and specifications, We have all specifications,Including UNS S44004 steel plate, UNS S44004 sheet, UNS S44004 square steel, UNS S44004 flat bar,UNS S44004 round bar,UNS S44004 forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the UNS S44004 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade UNS S44004 and Standards

 C(%): 0.95~1.20
Si(%): ≤1.00
Mn(%): ≤1.00
P(%)≤: 0.04
S(%)≤: 0.03
Cr(%): 16.0~18.0
Ni(%): —
Mo(%): ≤0.75

Machining performance

Download UNS S44004 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

Hot tags:UNS S44004 steel plate, UNS S44004 sheet, UNS S44004 square steel, UNS S44004 flat bar,UNS S44004 round bar,UNS S44004 forgings