Our to produce better steel-based products are the main used in industrial manufacturing various types High temperature high strength alloy and high-temperature alloyX6CrNiTi plate,X6CrNiTi Round Bar,X6CrNiTi forgings,X6CrNiTi suppliers, X6CrNiTi Stock,X6CrNiTi sheet, X6CrNiTi flat bar, X6CrNiTi pipe,X6CrNiTi tube,X6CrNiTi mould,X6CrNiTi round ingot,X6CrNiTi cold-rolled steel,X6CrNiTi coil,X6CrNiTi strap steel,X6CrNiTi hot-rolled steel,X6CrNiTi medium plate, X6CrNiTi heavy plate,X6CrNiTi shapped bar,X6CrNiTi hexahedral bar,X6CrNiTi,X6CrNiTi slab ingot,X6CrNiTi slab,X6CrNiTi price,X6CrNiTi square bar,X6CrNiTi square steel,X6CrNiTi wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of X6CrNiTi.

Current Location:Home » Products » High temperature high strength alloy and high-temperature alloy » X6CrNiTi

Product category

X6CrNiTi

Data Table for:Products: High temperature high strength alloy and high-temperature alloy:X6CrNiTi

X6CrNiTi properties and heat treatment forged piece, Including X6CrNiTi application and specifications, We have all specifications,Including X6CrNiTi steel plate, X6CrNiTi sheet, X6CrNiTi square steel, X6CrNiTi flat bar,X6CrNiTi round bar,X6CrNiTi forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the X6CrNiTi has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade X6CrNiTi and Standards

A basic introduction,
X6CrNiTi Introduces basic Introduces basic


Second, chemical composition
X6CrNiTi Chemical composition there environment
Carbon C: more than 0.08
Si: more than 1.0 silicon
Manganese Mn: more than 2.0
P: more than 0.045 P
S: more than 0.030 sulfur
Dr. QQ: 7888839

Chromium Cr: 17.00 ~ 19.00
Mo: avoid measurement molybdenum
Ni Ni: 9.0 ~ 12.0
Copper Cu: avoid measurement
Other: Ti5 * C ~ 0.80


Third, physical properties
X6CrNiTi Physical properties of the Physical properties
X6CrNiTi tensile test:
Steel thickness (mm) : from the point of measuring the yield point yield (MPa) sigma s: acuity 200 tensile strength tensile strength (MPa) sigma b: 500 ~ 730, dr QQ: 7888839


Four, material cross-references
X6CrNiTi material that will offer an Products of the table
Reference standard standard instead:
China GB13296-91 0 Cr18Ni10Ti

Material that will offer an Products: table
China GB13296-91 0 Cr18Ni10Ti
Dr. QQ: metal website administrator, 234827290.


Japan JIS G3463-94 SUS321TB SUS321HTB
The United States ASTM A213M-94 bASTM A249M-94 aASTM A269-94 aASTM A632-90 TP321H TP321H TP321 TP321
British BS3605Part1-1991-1992 321 321 BS3606 S31 S31
German DIN 17457-85 17458 85 X6CrNiTi DIN 1810 X6CrNiTi 1810 shenzhen DE dashing metal (Hong Kong) Co., LTD
The French NF A49 217:1987-218:1979 NF A49 TUZ6CNT 18 ~ 10 TUZ6CNT 18 ~ 10
ISO ISO 2604 out of the 75 TS 53


Five, the price
X6CrNiTi supplier Suppliers-X6CrNiTi prices

Six, production process
X6CrNiTi Production process Production mode


Seven, characteristic USES
X6CrNiTi characteristic Features use assumptions


Eight, heat treatment process
X6CrNiTi Heat treatment of Heat treatment process
 




Machining performance

Download X6CrNiTi the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.