Our to produce better steel-based products are the main used in industrial manufacturing various types Spring steelh24 plate,h24 Round Bar,h24 forgings,h24 suppliers, h24 Stock,h24 sheet, h24 flat bar, h24 pipe,h24 tube,h24 mould,h24 round ingot,h24 cold-rolled steel,h24 coil,h24 strap steel,h24 hot-rolled steel,h24 medium plate, h24 heavy plate,h24 shapped bar,h24 hexahedral bar,h24,h24 slab ingot,h24 slab,h24 price,h24 square bar,h24 square steel,h24 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of h24.

Current Location:Home » Products » Spring steel » h24

Product category

h24

Data Table for:Products: Spring steel:h24

h24 properties and heat treatment forged piece, Including h24 application and specifications, We have all specifications,Including h24 steel plate, h24 sheet, h24 square steel, h24 flat bar,h24 round bar,h24 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the h24 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade h24 and Standards

Mechanical Properties

Properties
 Conditions 
T (°C)
Treatment
Density (×1000 kg/m3)
1.77-1.83
25
 
Poisson's Ratio
0.35
25
 
Elastic Modulus (GPa)
44.8
25
 
Tensile Strength (Mpa)
290.0 
25 
H24 (sheet, plate) 
Yield Strength (Mpa)
220.0 (180.0) 
Elongation (%)
15.0 
Reduction in Area (%)
 
Note: Value in parentheses indicates yield strength for compression.
Hardness (HB500)
73 
25 
H24 (sheet, plate) 
Shear Strength (MPa)
160 
25 
H24 (sheet, plate

 Thermal Properties

Properties
 Conditions 
T (°C)
Thermal Expansion (10-6/ºC)
26 
20-100
Thermal Conductivity (W/m-K)
96.23 
0 

 




Machining performance

Download h24 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:h24 steel plate, h24 sheet, h24 square steel, h24 flat bar,h24 round bar,h24 forgings