Our to produce better steel-based products are the main used in industrial manufacturing various types Mould steel90MnCrV8 plate,90MnCrV8 Round Bar,90MnCrV8 forgings,90MnCrV8 suppliers, 90MnCrV8 Stock,90MnCrV8 sheet, 90MnCrV8 flat bar, 90MnCrV8 pipe,90MnCrV8 tube,90MnCrV8 mould,90MnCrV8 round ingot,90MnCrV8 cold-rolled steel,90MnCrV8 coil,90MnCrV8 strap steel,90MnCrV8 hot-rolled steel,90MnCrV8 medium plate, 90MnCrV8 heavy plate,90MnCrV8 shapped bar,90MnCrV8 hexahedral bar,90MnCrV8,90MnCrV8 slab ingot,90MnCrV8 slab,90MnCrV8 price,90MnCrV8 square bar,90MnCrV8 square steel,90MnCrV8 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 90MnCrV8.

Current Location:Home » Products » Mould steel » 90MnCrV8

Product category

90MnCrV8

Data Table for:Products: Mould steel:90MnCrV8

90MnCrV8 properties and heat treatment forged piece, Including 90MnCrV8 application and specifications, We have all specifications,Including 90MnCrV8 steel plate, 90MnCrV8 sheet, 90MnCrV8 square steel, 90MnCrV8 flat bar,90MnCrV8 round bar,90MnCrV8 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 90MnCrV8 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 90MnCrV8 and Standards

Step Shaft 90MnCrV8 Tube 90MnCrV8 Pie-shaped 90MnCrV8 Ring 90MnCrV8 Module 90MnCrV8 Large valves of the main 90MnCrV8 Other Profiled Forgings 90MnCrV8

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

Forging/hot rolling/ extrusion of steel

Specifications

Round bar steel: 1mm to 2000mm

Square-shape steel: 50mm  to  600mm

Plate steel:0.1mm  to  800mm

Width: 10mm to 1500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot Forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirement

Excellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.




Machining performance

Download 90MnCrV8 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:90MnCrV8 steel plate, 90MnCrV8 sheet, 90MnCrV8 square steel, 90MnCrV8 flat bar,90MnCrV8 round bar,90MnCrV8 forgings