Our to produce better steel-based products are the main used in industrial manufacturing various types Spring steelAISI 6150 plate,AISI 6150 Round Bar,AISI 6150 forgings,AISI 6150 suppliers, AISI 6150 Stock,AISI 6150 sheet, AISI 6150 flat bar, AISI 6150 pipe,AISI 6150 tube,AISI 6150 mould,AISI 6150 round ingot,AISI 6150 cold-rolled steel,AISI 6150 coil,AISI 6150 strap steel,AISI 6150 hot-rolled steel,AISI 6150 medium plate, AISI 6150 heavy plate,AISI 6150 shapped bar,AISI 6150 hexahedral bar,AISI 6150,AISI 6150 slab ingot,AISI 6150 slab,AISI 6150 price,AISI 6150 square bar,AISI 6150 square steel,AISI 6150 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 6150.

Current Location:Home » Products » Spring steel » AISI 6150

Product category

AISI 6150

Data Table for:Products: Spring steel:AISI 6150

AISI 6150 properties and heat treatment forged piece, Including AISI 6150 application and specifications, We have all specifications,Including AISI 6150 steel plate, AISI 6150 sheet, AISI 6150 square steel, AISI 6150 flat bar,AISI 6150 round bar,AISI 6150 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI 6150 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI 6150 and Standards

AISI 6150 is an oil quenching spring steel which offers good wear resistance after heat treatment.

TYPICAL ANALYSIS

C.
Mn.
Cr.
V.
0.50%
0.75%
1.00%
0.15%

 

 
Forging:
Forge AISI 6150 at 1050°C. Do not work this steel when it has fallen below 840°C.

Annealing:
Slow furnace cool from 840°/860°C.

Hardening:
Pre heat slowly to 650/700
°C and thoroughly soak the AISI 6150 component. Continue heating to the final hardening temperature of 850/870°C and allow the AISI 6150 component to be heated through. Quench in oil.

Tempering:
Temper immediately after quenching whilst tools are still hand warm. Re-heat to the tempering temperature, soak for one hour per 25 millimetre of total thickness, 2 hours minimum, then cool in air. For most applications tempering of AISI 6150 will be between 400°/600°C.

Tempering °C

  100

 
  200
  300
   400
450
500
550
600
HRc
56
53
50
  49
46
44
40
36




Machining performance

Download AISI 6150 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.