Our to produce better steel-based products are the main used in industrial manufacturing various types Heat resistant steelNCF800TB plate,NCF800TB Round Bar,NCF800TB forgings,NCF800TB suppliers, NCF800TB Stock,NCF800TB sheet, NCF800TB flat bar, NCF800TB pipe,NCF800TB tube,NCF800TB mould,NCF800TB round ingot,NCF800TB cold-rolled steel,NCF800TB coil,NCF800TB strap steel,NCF800TB hot-rolled steel,NCF800TB medium plate, NCF800TB heavy plate,NCF800TB shapped bar,NCF800TB hexahedral bar,NCF800TB,NCF800TB slab ingot,NCF800TB slab,NCF800TB price,NCF800TB square bar,NCF800TB square steel,NCF800TB wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of NCF800TB.

Current Location:Home » Products » Heat resistant steel » NCF800TB

Product category

NCF800TB

Data Table for:Products: Heat resistant steel:NCF800TB

NCF800TB properties and heat treatment forged piece, Including NCF800TB application and specifications, We have all specifications,Including NCF800TB steel plate, NCF800TB sheet, NCF800TB square steel, NCF800TB flat bar,NCF800TB round bar,NCF800TB forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the NCF800TB has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade NCF800TB and Standards

Grade :   KHN32T   ( ХН32Т ) (   Х20Н32Т     ЭП670   )
      Classification :   Hidh-temperature or heat-resistant alloy
      Equivalent steels:  
Chemical composition in % for grade   KHN32T   ( ХН32Т ) GOST   5632 - 72
Fe C Si Mn Ni S P Cr Ti Al
41.4 - 50.75 max   0.05 max   0.7 max   0.7 30 - 34 max   0.02 max   0.03 19 - 22 0.25 - 0.6 max   0.5

Mechanical properties under Т=20oС for grade   KHN32T   ( ХН32Т ) "
Assortment Dimension Direct. sв sT d5 y KCU Heat treatment
- mm - MPa MPa % % kJ / m2 -
Bar   longitudinal 480 180 40 60   Heating 1100 - 1150oC,Cooling air,
Sheet   dihedral 500 180 30     Heating 1080oC,Cooling water,
Forging     470 176 30 35    

Physical properties for grade   KHN32T   ( ХН32Т )
T E 10- 5 a 10 6 l r C R 10 9
Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m
20 2.05   15.9 8160    
100   13.7 13.4      
200   15.6 15.1      
300   17.2 16.7      
400   18 18      
500   18 19.2      
600   18.4 20.5      
700   18.9 21.7      
800   19 23.4      
T E 10- 5 a 10 6 l r C R 10 9

Equivalent steels for grade   KHN32T   ( ХН32Т )
USA Germany Japan France England European Spain Romania South Korea
- DIN,WNr JIS AFNOR BS EN UNE STAS KS
N08825
UNSNo8800
UNSNo8810
X10NiCrAlTi32-20
X2NiCrAiTi32-20
X5NiCrAlTi31-20
X8NiCrAlTi32-21
NCF2HTF
NCF800
NCF800TB
Z10NC32-21
Z8NC33-21
NA15
NA15H
X10NiCrAlTi32-21
X10NiCrAlTi32-20
X10NiCrAlTi32-20
X10NiCrAlTi32-21
X3CrMnNiN18-8-7
10TiAlCrNi320
NCF800

Specification :
Mechanical properties :
sв - Tensile strength , [MPa]
sT - Yield stress, [MPa]
d5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2]
HB - Brinell hardness , [MPa]

Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion (range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3]
C - Specific heat ( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]




Machining performance

Download NCF800TB the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.