Our to produce better steel-based products are the main used in industrial manufacturing various types Low alloy high-temperature steelUNS G41180 plate,UNS G41180 Round Bar,UNS G41180 forgings,UNS G41180 suppliers, UNS G41180 Stock,UNS G41180 sheet, UNS G41180 flat bar, UNS G41180 pipe,UNS G41180 tube,UNS G41180 mould,UNS G41180 round ingot,UNS G41180 cold-rolled steel,UNS G41180 coil,UNS G41180 strap steel,UNS G41180 hot-rolled steel,UNS G41180 medium plate, UNS G41180 heavy plate,UNS G41180 shapped bar,UNS G41180 hexahedral bar,UNS G41180,UNS G41180 slab ingot,UNS G41180 slab,UNS G41180 price,UNS G41180 square bar,UNS G41180 square steel,UNS G41180 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS G41180.

Current Location:Home » Products » Low alloy high-temperature steel » UNS G41180

Product category

UNS G41180

Data Table for:Products: Low alloy high-temperature steel:UNS G41180

UNS G41180 properties and heat treatment forged piece, Including UNS G41180 application and specifications, We have all specifications,Including UNS G41180 steel plate, UNS G41180 sheet, UNS G41180 square steel, UNS G41180 flat bar,UNS G41180 round bar,UNS G41180 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the UNS G41180 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade UNS G41180 and Standards

AISI 4118 steel, annealed at 870°C (1600°F), furnace cooled at 11°C (20°F)/hour, 25 mm (1 in.) round
Categories: Metal; Ferrous Metal; Alloy Steel; AISI 4000 Series steel; Low Alloy Steel; Carbon Steel; Low Carbon steel
Material Notes: Oil quenched. Forging temp.: 1230°C (2250°F) max. Carburizing temp.: 885 - 925°C. Hardening temp.: 830°C. Tempering temp.: 120 - 185°C.
Key Words: Alloy Steels, UNS G41180, ASTM A322, ASTM A331, ASTM A505, ASTM A519

Physical Properties Metric English Comments
Density  7.85 g/cc 0.284 lb/in³
 
Mechanical Properties Metric English Comments
Hardness, Brinell  137 137
Hardness, Knoop  156 156 Converted from Brinell hardness.
Hardness, Rockwell B  75 75 Converted from Brinell hardness.
Hardness, Vickers  143 143 Converted from Brinell hardness.
Tensile Strength, Ultimate  517 MPa 75000 psi
Tensile Strength, Yield  365 MPa 52900 psi
Elongation at Break  33.0 % 33.0 % in 50 mm
Reduction of Area  63.7 % 63.7 %
Modulus of Elasticity  205 GPa 29700 ksi Typical for steel
Bulk Modulus  140 GPa 20300 ksi Typical for steel
Poissons Ratio  0.290 0.290 Calculated
Machinability  60 % 60 % hot rolled and cold drawn. Based on 100% machinability for AISI 1212 steel.
Shear Modulus  80.0 GPa 11600 ksi Typical for steel
 
Electrical Properties Metric English Comments
Electrical Resistivity  0.0000245 ohm-cm 0.0000245 ohm-cm Typical 4000 series steel
 
Thermal Properties Metric English Comments
Specific Heat Capacity  0.475 J/g-°C 0.114 BTU/lb-°F Typical 4000 series steel
Thermal Conductivity  44.5 W/m-K 309 BTU-in/hr-ft²-°F Typical steel
 
Component Elements Properties Metric English Comments
Carbon, C  0.18 - 0.230 % 0.18 - 0.230 %
Chromium, Cr  0.40 - 0.60 % 0.40 - 0.60 %
Iron, Fe  97.7 - 98.49 % 97.7 - 98.49 % As remainder
Manganese, Mn  0.70 - 0.90 % 0.70 - 0.90 %
Molybdenum, Mo  0.080 - 0.15 % 0.080 - 0.15 %
Phosphorous, P  <= 0.035 % <= 0.035 %
Silicon, Si  0.15 - 0.35 % 0.15 - 0.35 %
Sulfur, S  <= 0.040 % <= 0.040 %

Users viewing this material also viewed the following:
AISI 4118 Steel, normalized at 910°C (1670°F), air cooled, 14 mm (0.55 in.) round
AISI 4118 Steel, normalized at 910°C (1670°F), air cooled, 25 mm (1 in.) round
AISI 4118 Steel, normalized at 910°C (1670°F), air cooled, 100 mm (4 in.) round
Overview of materials for AISI 4000 Series Steel
AISI 4118 Steel, normalized at 910°C (1670°F), air cooled, 50 mm (2 in.) round

M4118A / 7461
 




Machining performance

Download UNS G41180 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.